Glass fiber Rod for optical cables
FRP: Fiber Reinforced Polymer/Plastic
Glass fiber reinforced core for optical cables
1, Round FRP from Dia0.90mm to Dia5.00mm
Specifications: Diameters from 0.90mm to 5.00mm.
Roll Length from 15kms to 50kms with no joints.
Minimum Tensile strength:1100mpa
Minimum Tensile Modulus: 50mpa.
Minimum Flexural Strength: 1100mpa.
Minimum Flexural Modulus: 50mpa.
Maximum Elongation at break: 4%
Coefficient of linear thermal expansion(from -30
ºC to 80ºC): Max 8x10
-6/
ºC
Diameter Tolerance: +/-2%
Minimum Bending Radius
:40xD mm
.
Density: 2.05 --2.15g/cm3
High Temperature Bending Test(50
ºC,10
0ºC,120h): No bur, cracks or breaks.
2, Round FRP Dia0.40mm & Dia0.50mm
Specifications: Diameters 0.40mm & 0.50mm.
Roll Length from 25kms to 50kms with no joints.
Minimum Tensile strength:1280mpa
Minimum Tensile Modulus: 46mpa.
Minimum Flexural Strength: 1100mpa.
Minimum Flexural Modulus: 50mpa.
Maximum Elongation at break: 3%
Coefficient of linear thermal expansion(from -30
ºC to 80ºC): Max 8x10
-6/
ºC
Diameter Tolerance: +/-2%
Minimum Bending Radius
:18xD mm
.
Density: 2.05 --2.15g/cm3
High Temperature Bending Test(80
ºC,24h): Minimum 38xDmm
3, Flat FRP from 0.6X1.3mm to 10x3mm.
Specifications: from flat 0.6x1.3mm to 10x3mm.
Roll Length from 5kms to 50kms with no joints.
Minimum Tensile strength:1200mpa
Minimum Tensile Modulus: 48mpa.
Maximum Elongation at break: 3%
Tolerance of both Width and Thickness: +/-2%
Minimum Bending Radius
:30xT mm
.
Density: 2.05 --2.15g/cm3
High Temperature Bending Test(100
ºC,24h):Minimum 8xT mm.